Behaviour of stress corrosion cracking of austenitic stainless steels in sodium chloride solutions
Samir Milad, Elsariti; Haftirman, Dr. (Elsevier B.V., 2013)Click Stress Corrosion Cracking (SCC) is an environmentally well-known as a failure caused by exposure to a corroding while under a sustained tensile stress. SCC is most often rapid, unpredictable. Failure can occur in a ... -
Effect of roughness of hypo-and hyper-eutectic Al-Si piston alloy on wear characteristics under lubrication
Riyadh A., Al-Samarai; Haftirman, Dr.; Khairel Rafezi, Ahmad, Dr.; Yarub, Al-Douri, Assoc. Prof. Dr. (Elsevier B.V., 2013)The tribological behavior of tow Al-Si alloys under the influence of surface roughness average was investigated for the present study. The silicon content of these alloys ranged 10 and 16-wt% Si, and includes hypoeutectic ... -
Evaluate the effects of various surface roughness on the tribological characteristics under dry and lubricated conditions for Al-Si alloy
Riyadh A., Al-Samarai; Haftirman, Dr.; Khairel Rafezi, Ahmad, Dr.; Yarub, Al-Douri, Assoc. Prof. Dr. (Scientific Research Publishing Inc. All rights reserved., 2012-07)The effect of surface roughness average of hypereutectic aluminum silicon alloys (with 16 wt% Si) on the friction and wear was investigated. Various surface roughness average (Ra) of different degrees was verified as well ... -
Fatigue crack initiation and growth of aluminum alloy with stress ratio effects
Haftirman, Idrus, Dr.; Afendi, M.; Wong, Chun Hoe (Trans Tech Publications, 2014)Fatigue crack initiation and growth of aluminum alloys with stress ratio were investigated due to it was widely used in aircraft production parts. Various types of aluminium alloy have been selected (6063-T6, 7075-T6, and ... -
Tribological properties of WS2 nanoparticles lubricants on aluminum-silicon alloy and carbon steels
Riyadh A., Al-Samarai; Yarub, Al-Douri, Assoc. Prof. Dr.; Haftirman, Dr.; Khairel Rafezi, Ahmad, Dr. (Walailak University, 2013-06)The rheological properties of nanometric tungsten disulphide (WS2) nanoparticles oil lubricants and its tribological performance with two hypereutectic Al-Si alloy and carbon steel are examined. These two oils are used to ...