Ferrous base materials performance in seawater and its failure analysis
(Kolej Universiti Sains dan Teknologi Malaysia, 2004)
The effect of seawater to the corrosion behavior of ferrous base steel AISI 1053 have been determined at room temperature. The corrosion products were characterized by using energy-dispersed X-ray spectroscopy (EDS), and ...
Hot corrosion behaviour of Nickel-200 alloy in presence of Sodium salts at 850°C
(Academy Science Publishers/African Academy of Sciences (AAS), 1996)
The hot corrosion behaviour of Nickel-200 industrial alloy has been investigated in presence of Na2S04, NaCI, NaN03, Na2C03 and Na202 at 850°C in flowing air. The hot corrosion kinetic and effect of salt deposition on the ...
Oxidation behaviour of 18/8 Cr-Ni austenitic steel in presence of Na2SO4 and NiSO4 at 650 to 1000°C
(Carl Hanser Verlag, Germany, 1983)
Iron based alloys containing chromium as a major constituent with nickel additions are the most prominent materials in coal fired generating units and petroleum refinery plants. The corrosion of these alloys under service ...
Oxidation behavior of Sodium-, Calcium- and Potassium- Sulphates coated Fe-20Cr alloy at 800°C
(Chinese Electronic Periodical Services, 1997-04)
The effect of Na2S04, CaS04,K2S04 and their mixture coatings on the high temperature oxidation behaviour of Fe-20Cr alloy at 800 C has been investigated. The data have been complemented by kinetic measurements, SEM ...
Effect of Sodium Nitrate and Sodium Peroxide deposits on high temperature oxidation of Nimonic-105 Alloy at 700 C *
(Chinese Electronic Periodical Services, 1995)
The effect of sodium nitrate (NaN03) and sodium peroxide (Na202) deposits on the high temperature oxidation of Nimonic-105 (N-105) alloy at 700rj has been studied for a period of 120 h in air. The alloy was more severely ...
Oxidation behavior of SAE-1053 alloy in presence of seawater
(INSInet Publication, 2009-01)
The oxidation behavior of steel SAE-1053 alloy were investigated in presence of seawater at atmospheric condition. The rate of corrosion was varied with the water movements and the aeration. The scale morphologies were ...