The anodizing of sintered Mg/Ca alloys
(Universiti Malaysia Perlis (UniMAP)School of Materials Engineering, 2016-06)This project is focusing on the effect of anodizing on the sintered Mg/Ca alloys. The Mg/Ca alloy was fabricated using powder metallurgy method. The Mg powder was mixed with 1 wt.% Ca powder using rotating mill with ball ... -
The effect of alloying elements in sintered-recycle steel compaction
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)Effects of alloying elements in the sintered-recycle steel compaction were studied using powder metallurgy technique. High-energy milling technique was used to crush and mill the waste steel chip in the form of spiral ... -
The effect of cooling condition on the microstructure and properties of Al-4.4Cu-0.8Si-0.5Mg powder compacts
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)The aim of this research is to study the effect of cooling condition on microstructure and properties of Al alloy. Powder compacts from a premixed commercial aluminium powder Al-4.4Cu-0.8Si-0.5Mg (wt %) grade have been ... -
Effect of grinding media size and shape on the iron mill scale particle and properties
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-05)A study was undertaken to determine how the effect of grinding media size and shape on the iron mill scale particle size and properties. Comparative tests were conducted using the two types of grinding media which are ... -
The effect of HAP addition on the physical and mechanical properties of co-cr-mo/HAP composites for biomedical apllications
(Universiti Malaysia Perlis (UniMAP)School of Materials Engineering, 2015-11)This paper reports on the effect of HAP addition on the physical and mechanical properties of Co-Cr-Mo/HAP composites fabricates by powder metallurgy. Co-Cr-Mo is used in orthopedic because of its excellent biocompatibility ... -
The effect of heat treatment on Fe-Ni/SiC composite
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)The mechanical properties of Fe-Ni/SiC composite on five different soaking time were studied. The Fe-Ni/SiC composite consist of 78% Fe, 20% SiC and 2% Ni. The Fe-Ni/SiC composite was fabricated using powder metallurgy ... -
Microstructure of development Al-Mg-Si-Cu powder metallurgy under different addition of Sn
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)This project involve 3 sample types that had labeled as Premix A (1%Sn addition), Premix B (1.5%Sn addition) and Premix C (2.0%Sn), each types have five samples. After compaction process measured the weight, thickness, ... -
Sintering behavior and microstructural characterization of Aluminium copper powder compacts (Al- 4.4 Cu-0.8 Si-0.5 Mg Wt% ) alloy prepared by powder metallurgy
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-05)Powder Metallurgy (P/M) is a near net shape metal forming techniques used to manufacture part to close tolerance. In this research, aluminium copper alloy (Al-4.4%Cu- 0.8% Si-0.5%Mg) is prepared by using P/M method. In ... -
Study of fabrication Al-Tin slag composite by powder metallurgy method
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-05)In the present investigation, Aluminum-tin slag composite have been produced by powder metallurgy (P/M) route. Aluminum (Al) and tin slag were undergo milling and sieving process where particle size <75 µm and <63 µm for ... -
A study of hardcoat anodizing on PM Al-Mg composite
(University Malaysia PerlisSchool of Materials Engineering, 2008-05)This research is being conducted to investigate an effect occurring on anodizing process on powder metallurgy Aluminium-Magnesium (PM Al-Mg) composite. Composite materials are fabricated by using powder metallurgy method ... -
A study of microstructure and mechanical properties of copper filled Polypropylene and copper filled Epoxy
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)In this project, metal filled polymer composite had been produced by using powder metallurgy concept and cold pressing method. The processing method had influenced the properties of composite system and to establish the ... -
Synthesis and characterization of Fe-Al alloy with different sintering temperature
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)The iron aluminides Fe3Al and FeAl3 have been among the most widely studied intermetallics because of their low cost, low density, good wear resistance, ease of fabrication and resistance to oxidation and corrosion. A ...