Strength of the weld line and warpage defects on the molded parts in injection molding process
Date
2013Author
S. M., Nasir
Khairul Azwan, Ismail, Dr.
Shayfull Zamree, Abd Rahim
Norshah Afizi, Shuaib
Metadata
Show full item recordAbstract
Strength at weld the line location and warpage problem in injection molding plastic component were not new problems in injection molding industries. Many researchers had emerged with several improvement techniques to reduce these problems that been applied to a verity of customer products that injected with various types of polymers. This paper reviewed the improvement techniques previously studied to maximize strength at weld line location and minimize warpage or deflections of the molded parts. From the review, it can be seen that by using mechanical and thermal assistance during injection molding process, and the optimization of machine parameters for stated problems can be improved. However, there was lack on the multi objectives optimization which should be apply to ensure the weld line and warpage were improved together to get the best quality products.
URI
http://www.praiseworthyprize.org/latest_issues/IREME-latest/IREME_vol_7_n_5.htmlhttp://dspace.unimap.edu.my:80/dspace/handle/123456789/34733
Collections
- Norshah Afizi Shuaib, Dr. [19]
- Shayfull Zamree Abd Rahim, Assoc. Prof. Ir. Dr. [42]
- School of Manufacturing Engineering (Articles) [125]
- Center of Excellence for Geopolymer and Green Technology (CEGEOGTECH) (Articles) [135]
- School of Materials Engineering (Articles) [560]
- Khairul Azwan Ismail, Associate Professor Dr. [22]