Development of dense hydroxyapatite-ni by modified electroless deposition technique.
Date
2014Author
Sri Asliza, Md Amin
Mohd Zaheruddin, Kasmuin
Azmi, Rahmat, Dr.
Shamsul Baharin, Jamaludin, Prof. Dr.
Khairel Rafezi, Ahmad, Dr.
Metadata
Show full item recordAbstract
Ni deposited on HA powder was prepared by electroless plating process without sensitization and activation treatment. The deposited powder obtained was characterized by energy dispersive spectroscopy (EDX) and x-ray diffraction (XRD). The microstructure and hardness of the sintered powder were examined by scanning electron microscopy (SEM) and Vickers hardness respectively. From the result, the nickel existence in the deposition was confirmed by the EDX analysis. The diffraction peaks at 44.5 and 64.7o (2θ) of planes (111) and (211) respectively were belong to nickel. Nickel are homogeneously dispersed in HA matrix with grain size between 0.25-2μm after sintered at 1250°C. The improvement of 93% and 180% in average hardness and flexural strength respectively were achieved with nickel presence in HA compared to pure HA.