This paper studied the influence of activator composition on the properties of calcined kaolin geopolymeric powder. The alkaline activation of calcined kaolin was performed in mixture of waterglass liquid and NaOH solution ...

This paper reported the properties of kaolin geopolymers in term of the bulk density, compressive strength, qualitative observation and SEM analysis of the kaolin geopolymers. Kaolin geopolymers were synthesized through ...

This paper presents the development of a nano geopolymer for sustainable concrete using fly ash synthesized by high-energy ball milling. In this paper, we report on our investigation of the effects of grinding on the binder ...

This paper covers the results of X-ray powder diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) in assessing the phase identification and functional group of kaolin geopolymer based on the different ...

Effective Microorganism (EM) technology was found as the credible solution to solve many environmental problems including wastewater issues. The EM which is in the form of EM mud ball was tested to be effectively used for ...

Kaolin geopolymers were produced by the alkali-activation of kaolin with an activator solution (a mixture of NaOH and sodium silicate solutions). The NaOH solution was prepared at a concentration of 6-14 mol/L and was mixed ...

Oxide molar ratios are the main key parameter determining the performance of a kaolin geopolymers. The kaolin composition and various mixture proportions will lead to different oxide molar ratios in geopolymer system. In ...

Geopolymer is cementitious binders that do not require the presence of ordinary Portland cement (OPC). Fly ash with geopolymer formulations prepared with mixing alumino-silicate with the alkaline activator solution has ...

Natural fibers reinforced polymer composites have gained more interest because of their biodegradable, light weight, less expensive sources, easy processing, high specific modulus and also environmentally friendly appeal. ...

Geopolymer is cementitious binders that do not require the presence of ordinary Portland cement (OPC). Class F fly ash with geopolymer formulations prepared with an alkaline activator (mixture of Na2SiO3 and NaOH solutions) ...