Study the effect of replacement of fly ashon ordinary portland cement
(Universiti Malaysia Perlis (UniMAP), 2016-05)
The replacement of fly ash in Ordinary Portland cement have been conducted to measure the strength of concrete in different ratio between fly ash and cement. This research is involved three stage like Raw material analysis, ...
A study on the purification of Limestone
(Universiti Malaysia Perlis (UniMAP), 2016-06)
This research study focused on the purification of limestone by multiple reprecipitation. This study involves the application of different temperature for
carbonation process as to observe the reactiveness of particles ...
Beneficiation and extraction of Malaysian's iron ores
(Universiti Malaysia Perlis (UniMAP), 2016-06)
This present study is to study the influence of the different sizes of iron ore from
Bukit Besi, Terengganu and Kulim, Kedah on the reduction process with coke from
Perwaja Steel, Kemaman, Terengganu as a reducing agent. ...
The anodizing of sintered Mg/Ca alloys
(Universiti Malaysia Perlis (UniMAP), 2016-06)
This project is focusing on the effect of anodizing on the sintered Mg/Ca alloys.
The Mg/Ca alloy was fabricated using powder metallurgy method. The Mg powder was
mixed with 1 wt.% Ca powder using rotating mill with ball ...
Controlling the synthesis parameter during Fe(OH)₂ precipitation for goethite formation
(Universiti Malaysia Perlis (UniMAP), 2016-05)
Iron oxide were synthesized goethite free of magnetic impurities with different crystal
sizes in different molar ratio and mixing time through the reverse precipitation of
FeSO₄∙7H₂O and NaOH. Mostly goethite mineral ...
Preparation and characterization of LDPE/TPS blend filled with calcium carbonate
(Universiti Malaysia Perlis (UniMAP), 2016-05)
The characterization of LDPE/TPS composite with calcium carbonate (CaCO₃)
filler was conducted under several measurements such as tensile testing, scanning
electron microscopy (SEM), Thermogravimetric Analysis (TGA) and ...
Effect of high temperature exposure on Kaolin geopolymer
(Universiti Malaysia Perlis (UniMAP), 2016-06)
The geopolymer material is a green material which produce less emission of CO2
and less energy consuming material compare to Portland Cement (PC) materials. An
experimental study the effect of high temperature exposure ...
Observation on the reduction of Iron Oxide by graphite and coke
(Universiti Malaysia Perlis (UniMAP), 2016-06)
This present study is to investigate the reduction of iron oxide with metallurgical coke and graphite used in this project. The purpose of this study mainly was to investigate the possibilities of reducing hematite to ...
Effect of solution treatment temperature on the microstructure of Fe-40Ni-24Cr alloy
(Universiti Malaysia Perlis (UniMAP), 2016-06)
The research study describes the effect of solution treatment temperature on
the microstructure of Fe-40Ni-24Cr alloy. The working process is divided into three
(3) working phases which are solution treatment process, ...
Synthesis and mechanical properties of alumina slip casting from aluminum tri-hydrate (Al(OH)₃
(Universiti Malaysia Perlis (UniMAP), 2016-05)
This experiment was done to investigate the mechanical properties of synthesized
Al(OH)₃ for slip casting process. The Al(OH)₃ precursor was synthesized by two process,
calcinations of Al(OH)₃ and leaching along with ...