Preparation of submicron Al-Ti Alloy particles by mechanical alloying
Abstract
Introduction:
Mechanical alloying (MA) is a solid-state powder processing technique involving repeated welding, fracturing and re-welding of powder particles in a high-energy ball mill [1-3]. MA has been used to synthesize equilibrium and non-equilibrium phases using elementary or pre-alloyed powder [4]. The advantages of using mechanical alloying for synthesis of crystalline materials are because of its simplicity, cost effectiveness, room temperature synthesis process, and capability of production on industrial scale [5-6]. A process control agent (PCA) is generally added to powder mixture during milling when the powder mixing involves a substantial fraction of a ductile component. PCAs are used to avoid adhesion of the powder to the ball and vials during MA processing. Mostly organic compounds, such as stearic acid, oxalic acid, hexane, ethanol and methanol are used as PCAs [6]. Among them, stearic acid is one of the most effective and very often used as a PCA. In this paper, it is reported the used of mechanical alloying process and stearic acid to prepare submicron of Al-Ti alloy particles.
Collections
- Conference Papers [2600]
Related items
Showing items related by title, author, creator and subject.
-
The effect of duration aging temperature on fatigue strength of aluminum alloy strength of aluminum alloy
Ahmad Syayuthi, Abdul Rahman; Haftirman; Teo, Ee Lynn (Universiti Malaysia Perlis (UniMAP)Pusat Pengajian Kejuruteraan Mekatronik, 2012-02-27)This paper present the effect of different duration aging temperature on fatigue strength of Al6063. Al 6063 alloy specimens have been solution heat treated at 520C for 2 hours. Subsequently, the artificial ageing heat ... -
Synthesis and characterization of Corroded anodized coating of Titanium base alloy, Austenitic steel and Aluminium base alloy commercially used
Lee Chee Hong (Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)Involving this project, several techniques used to study the morphological structure as well as characterization of corroded anodized coating of titanium base alloy, austenitic steel and aluminium base alloy commercially ... -
Effect of alloying elements (Ni and Cr) on density and hardness of Co alloy fabricated by powder metallurgy
Raudhah, Othman; Shamsul Baharin, Jamaludin; Mohd Nazree, Derman (Universiti Malaysia Perlisp.1-5, 2009-12-01)Influences of Ni and Cr addition on the properties of powder metallurgy Co base alloys were investigated. The alloys were produced by powder metallurgy technique and sintered under argon atmosphere. Scanning electron ...