Properties of lightweight concrete composites with mixture of fly ash and concrete sludge aggregate
Date
2014Author
Norlia, Mohamad Ibrahim
Roshazita, Che Amat
Shamshinar, Salehuddin
Nur Liza, Rahim
Abdul Rahim, Abdul Razak
Ooi, Wei Hong
Metadata
Show full item recordAbstract
Lightweight foamed concrete is a concrete made by cement slurry mixed with foam so that foamed concrete that is much lighter than conventional concrete can be produced. The objectives of this study is to develop optimal pre-foamed lightweight foamed concrete and to achieve desired density of lightweight concrete that is below 2400 kg/m3. Three samples of concrete were batching with 0%, 25% and 50% of foam respectively under mixing ratio of 1:1:2 and foam dilution ratio 1:5 to obtain optimum result. Based on the result attained, the samples achieved the bulk density ranged from 1943 kg/m3 to 2305 kg/m3. In addition, other physical characteristics of this mixture of materials show that its water absorption for all the samples was increased from 6.508% to 11.889%. This trend of results was obtained if the volume of foam presented in the concrete were increased. Furthermore, the samples achieved compression strength ranged from 22.418 MPa to 32.229 MPa with presence of foam. In summary, with additional of fly ash and concrete sludge as aggregate it can help to produce comparable concrete composites with lighter density.