C0-HA composite produced by simple electroless deposition method was studied. From the particle size analysis by Malvern particles analyzer its shows that 19% increment in average of the particle size powder increase after ...

HA-Ni composites were fabricated by uniaxial pressing from coated powders, in which HA particles were successfully coated with nickel precursor by the electroless deposition method. The compacted powders sintered at ...

Co-HA composite produced using electroless deposition without conventional sensitization and activation treatment was studied with varying sintering temperature (1100°C, 1200°C and 1250°C). The particles size, bulk density, ...

In this project, iron mill scale has been used to produce iron powder that can be used within the Powder Metallurgy process. To achieve this objective, the iron mill scale needs to be refined. This involve the work of ...

Ni deposited on HA powder was prepared by electroless plating process without sensitization and activation treatment. The deposited powder obtained was characterized by energy dispersive spectroscopy (EDX) and x-ray ...

Porous anodic alumina (PAA) has been produced on aluminium substrate by single-step anodising at 50 V in 0.3 M oxalic acid at 15°C for 60 min. The highly ordered pore and cell structure was achieved by subjecting the PAA ...