Corrosion performance of reinforcement bar in geopolymer concrete compare with its performance in ordinary portland cement concrete: A short review
(Trans Tech Publications, 2013)
Since decades ago, corrosion is the crucial factors for million dollars loss in construction industry. Corrosion of reinforcement bar in ordinary Portland cement (OPC) concrete is mainly due to chloride and acid attack and ...
Response of functionality graded hydroxyapatite/F-75 in saline solution 0.9% NaCl
(Trans Tech Publications, 2013)
Functionally graded hydroxyapatite (HAP) /F-75 was fabricated using powder metallurgy technique. Samples fabricated were tested inside 0.9% NaCl to check their bioactivity reaction. After immersed, samples were analyzed ...
High temperature corrosion behaviour of steel with a Carbonate deposit at 1123K
(2007)
The high temperature corrosion behavior of A1S1 304 austenitic stainless steel and S45C carbon steel were studied in presence with CaCO3 salt at 1123K for 24,48,72, 96 and 120 hour. The studies were carried out to determine ...
Ferrous base materials performance in seawater and its failure analysis
(Kolej Universiti Sains dan Teknologi Malaysia, 2004)
The effect of seawater to the corrosion behavior of ferrous base steel AISI 1053 have been determined at room temperature. The corrosion products were characterized by using energy-dispersed X-ray spectroscopy (EDS), and ...
Hot corrosion behaviour of Nickel-200 alloy in presence of Sodium salts at 850°C
(Academy Science Publishers/African Academy of Sciences (AAS), 1996)
The hot corrosion behaviour of Nickel-200 industrial alloy has been investigated in presence of Na2S04, NaCI, NaN03, Na2C03 and Na202 at 850°C in flowing air. The hot corrosion kinetic and effect of salt deposition on the ...
Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater
(Sadguru Publications, 2005)
The corrosion behavior of 8.6 Al-Cu alloy was investigated in 4 different conditions of South China Seawater. The weight loss curve of alloy increases with time during the initial exposure period, due to dissolution of ...
Hot corrosion behaviour of Austenitic Steel-308 in Chloride salts
(2008)
The intensification of process engineering in almost every branch of modern technology, and development of new technologies make increasingly higher requirements for metallic construction materials, especially for their ...
The CsCl- and CsN03-induced high temperature oxidation of Nimonic-90 alloy at 1123 K
(Elsevier Science B.V., 1996)
Nickel-base alloys find vital scope in space and nuclear applications due to their numerous favourable properties such as low density, high strength and corrosion resistance. The high temperature oxidation of Nimonic-90 ...
Corrosion behaviour of copper in various grades of palm oil
(Carl Hanser Verlag, 2008)
Hot corrosion behaviour of Inconel-600 alloy in presence of NaCI and Na2CO3 at 850°C
(Carl Hanser Verlag, 1993)