    • Alteration in the microstructure of fly ash geopolymer upon exposure to elevated temperatures 

      Omar A., Abdulkareem; Mohd Mustafa Al-Bakri, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr. (Trans Tech Publications, 2013)
      This paper represents the mechanical and microstructure changes in geopolymeric material synthesized by the alkali activation of locally source fly ash at high temperatures of 400, 600 and 800 °C. The high compressive ...
    • Calcined kaolin geopolymeric powder: Influence of water- to geopolymeric powder ratio 

      Liew, Yun Ming; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al Bakri, Abdullah; Binhussain, M.; Luqman, Musa, Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; cheng, Yong Heah (Trans Tech Publications, 2012-07)
      This paper describes the synthesis of calcined kaolin geopolymeric powder from the alkaline activation of calcined kaolin followed by solidification and pulverizing process. The geopolymeric powder was used by just adding ...
    • Characterization of LUSI mud volcano as geopolymer raw material 

      Mohd Mustafa Al Bakri, Abdullah; Rafiza, Abdul Razak; Djwantoro, Hardjito, Dr.; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr. (Trans Tech Publications, 2012)
      The mud of mud volcano samples were collected from an eruption site named 'LUSI' (Lumpur "mud" -Sidoarjo), East Java, Indonesia for characterization. Analysis showed that, the major constituents of mud are SiO 2 and Al 2O ...
    • Comparison of geopolymer fly ash and ordinary Portland cement to the strength of concrete 

      Mohd Mustafa Al Bakri, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohamed, Bnhussain, Prof. Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Rafiza, Abdul Razak; Zarina, Yahya (American Scientific Publishers, 2013-12)
      The aim of this study is to evaluate the effect of various fly ash: aggregate ratios by using fly ash (FA) based geopolymer compared to ordinary Portland cement (OPC) on the compressive strength of concrete. The different ...
    • Comparison of original and sintered LUSI mud from East Java, Indonesia as raw material for making a geopolymer 

      Rafiza, Abdul Razak; Mohd Mustafa Al Bakri, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Djwantoro, Hardjito, Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr. (American Scientific Publishers, 2013-01)
      This paper presents the characterization of LUSI mud from East Java, Indonesia, as a potential raw material for making a geopolymer. Two types of LUSI mud were analyzed, i.e., original LUSI mud and LUSI mud that had been ...
    • Correlating composition design and properties of calcined kaolin geopolymeric powder 

      Liew, Yun Ming; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al Bakri, Abdullah; Mohamed, Bnhussain, Prof. Dr.; Luqman, Musa, Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Che Mohd Ruzaidi, Ghazali, Prof. Madya; Heah, Cheng Yong (American Scientific Publishers, 2013-12)
      This paper discussed the relation between composition design and properties of calcined kaolin geopolymeric powder. Geopolymeric powder was produced by applying the geopolymerization process. The solids-to-liquid ratios ...
    • Correlation between Na 2SiO 3/NaOH ratio and fly ash/alkaline activator ratio to the strength of geopolymer 

      Mohd Mustafa Al Bakri, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Mohamed, Bnhussain, Prof. Dr.; Zarina, Yahya; Rafiza, Abdul Razak (Trans Tech Publications, 2012)
      Geopolymer requires an alkaline activator to induce it pozzolanic property and to accelerate the geopolymerisation process. The geopolymerisation process occurs due to the mixing of fly ash, sodium silicate and sodium ...
    • Design, processing and characterization of fly ash-based geopolymers for lightweight concrete application 

      Mohd Mustafa Al-Bakri, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Sandu, Andrei Victor; Mohamed, Bnhussain, Prof. Dr.; Zarina, Yahya; Rafiza, Abdul Razak (Institute for Scientific Information (ISI), 2013-04)
      The mix design of geopolymers plays important role in obtaining desirable compressive strength. Optimum mix design of geopolymers can be applied for application, such as lightweight concrete. In order to determine the ...
    • Effect of alkali concentration on mechanical properties of kaolin geopolymers 

      Heah, Cheng Yong; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al-Bakri, Abdullah; Mohamed, Bnhussain, Prof. Dr.; Luqman, Musa, Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Liew, Yun Ming (Procema SA, 2012)
      Alkali concentration is the most significant factor in geopolymerization process that must be taken into consideration during the synthesis of kaolin geopolymers. The kaolin geopolymers were prepared by mixing kaolin and ...
    • Effect of curing regimes on metakaolin geopolymer pastes produced from geopolymer powder 

      Liew, Yun Ming; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al Bakri, Abdullah; Mohammed, Bnhussain; Luqman, Musa; Khairul Nizar, Ismail, Prof. Madya Dr.; Che Mohd Ruzaidi, Ghazali, Prof. Madya; Cheng, Yong Heah (Scientific.Net/Trans Tech Publications, 2012-12)
      The properties of metakaolin geopolymer paste are affected by the alkali concentration, the initial raw materials, solidification process, and amount of mixing water as well as the curing conditions. This study aimed to ...
    • The effect of curing time on the properties of fly ash-based geopolymer bricks 

      Wan Mastura, W. I.; Kamarudin, Hussin, Brig. Jen. Datuk Prof. Dr.; Khairul Nizar, Ismail, Prof. Madya Dr.; Mohd Mustafa Al Bakri, Abdullah; Mohammed, Bnhussain (Scientific.Net/Trans Tech Publications, 2012-12)
      This paper reports the results of an experimental work conducted to investigate the effect of curing conditions on the properties of fly ash-based geopolymer bricks prepared by using fly ash as base material and combination ...
    • General properties of kaolin geopolymers 

      Heah, Cheng Yong; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al-Bakri, Abdullah; Mohamed, Bnhussain, Prof. Dr.; Luqman, Musa, Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Che Mohd Ruzaidi, Ghazali, Prof. Madya; Liew, Yun Ming (American Scientific Publishers, 2013-01)
      This paper reported the properties of kaolin geopolymers in term of the bulk density, compressive strength, qualitative observation and SEM analysis of the kaolin geopolymers. Kaolin geopolymers were synthesized through ...
    • The influence of curing periods on the compressive strength of fly ash-based geopolymer at different aging times 

      Omar A., Abdulkareem; Mohd Mustafa Al-Bakri, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Prof. Madya Dr. (Trans Tech Publications, 2012)
      The results of the current experimental investigation indicate the significant effect of the heating periods on the compressive strength of fly ash-based geopolymers prepared at different alkaline liquid content at both ...
    • Influence of dolomite on the mechanical properties of boiler ash geopolymer paste 

      Zarina, Yahya; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al-Bakri, Abdullah; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Rafiza, Abdul Razak (Trans Tech Publications, 2014)
      The waste material from palm oil industry has been increasing since Malaysia was the world largest exported of palm oil mill. The waste such as palm fibers, nut shells, palm kernel and empty fruit bunches are the solid ...
    • Influence of oxide molar ratios on kaolin geopolymers 

      Heah, Cheng Yong; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al-Bakri, Abdullah; Mohamed, Bnhussain, Prof. Dr.; Luqman, Musa, Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Che Mohd Ruzaidi, Ghazali, Prof. Madya; Liew, Yun Ming (American Scientific Publishers, 2013-12)
      Oxide molar ratios are the main key parameter determining the performance of a kaolin geopolymers. The kaolin composition and various mixture proportions will lead to different oxide molar ratios in geopolymer system. In ...
    • Kaolin-based geopolymers with various NaOH concentrations 

      Heah, Cheng Yong; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al-Bakri, Abdullah; Mohamed, Bnhussain, Prof. Dr.; Luqman, Musa, Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Che Mohd Ruzaidi, Ghazali, Prof. Madya; Liew, Yun Ming (Springer Verlag, 2013-03)
      Kaolin geopolymers were produced by the alkali-activation of kaolin with an activator solution (a mixture of NaOH and sodium silicate solutions). The NaOH solution was prepared at a concentration of 6-14 mol/L and was mixed ...
    • Lightweight fly ash-based geopolymer concrete 

      Omar A., Abdulkareem; Mohd Mustafa Al Bakri, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Prof. Madya Dr. (Trans Tech Publications, 2013)
      The experiments of this study were preformed to study the synthesis process for lightweight aggregate geopolymer concrete (LWAGC) using normal sand as a fine aggregate and expanded clay as lightweight aggregate. The LWAGC ...
    • Mechanical and microstructural evaluations of lightweight aggregate geopolymer concrete before and after exposed to elevated temperatures 

      Omar A., Abdulkareem; Mohd Mustafa Al-Bakri, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Mohamed, Bnhussain, Prof. Dr. (MDPI, Basel, Switzerland, 2013)
      This paper presents the mechanical and microstructural characteristics of a lightweight aggregate geopolymer concrete (LWAGC) synthesized by the alkali-activation of a fly ash source (FA) before and after being exposed to ...
    • Mechanical performances of fly ash geopolymer bricks 

      Wan Mastura, Wan Ibrahim; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Prof. Madya Dr.; Mohd Mustafa Al Bakri, Abdullah (American Scientific Publishers, 2013-01)
      Geopolymer is a new class of three-dimensionally networked amorphous to semi-crystalline alumino-silicate materials, and first developed by Professor Davidovits in 1978. Geopolymers can be synthesized by mixing alumino-silicate ...
    • Microstructure studies on the effect of the alkaline activators of fly ash-based geopolymer at elevated heat treatment temperature 

      Mohd Mustafa Al-Bakri, Abdullah; Omar A., Abdulkareem; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Rafiza, Abdul Razak; Zarina, Yahya; Alida, Abdullah (Trans Tech Publications, 2013)
      Fly ash-based geopolymers are new binding materials produced to replace the ordinary Portland cement (OPC) used in concrete. In this research, the effect of alkaline activators on the compressive strength and the microstructure ...