Selective extraction, separation and recovery of Cu(II) in presence of Zn(II) and Ni(II) from leach liquor of waste printed circuit board using microcapsules coated with Cyanex 272
(Springer Verlag, 2012-05)
The study was conducted to optimize the selective extraction and recovery of Cu(II) in the presence of Zn(II) and Ni(II) from the leach liquor of waste printed circuit boards (PCBs). The extraction experiments were carried ...
Microstructure and interface analysis of glass particulate reinforced aluminum matrix composite
(Trans Tech Publications (TTP), 2013)
A characterization of microstructure and interface was made on the composites Al- 4% Cu reinforced with 15 wt. % glass particulate. The composite was fabricated by powder metallurgy followed by solution treatment and ...
Characterization of porous aluminum fabricated via sintering- dissolution process (SDP)
(Trans Tech Publications, 2013)
Porous metals that have open pores structure with low density and light weight properties are suitable to be used in many engineering applications. In this work, the porous aluminum was fabricated via sintering dissolution ...
Effect of spot welding current and cycles on the mechanical properties of welded galvanized steel sheets
(Trans Tech Publications, 2013)
Studies on the effects of welding current and cycles were carried on the galvanized steel sheets using spot welding. The welding currents used were 3 kA, 5 kA 6 kA and the welding cycles were 4, 6 and 8. Tensile shear and ...
Compressive strength and crack propagation of cement composites reinforced coconut fibre
(Medwell Journals, 2012)
This study presents the compressive strength and crack propagation of cement composites reinforced coconut fibre. The development of cement composites in this research were done by substituting coconut fibre to the portion ...
Mechanical properties and fracture behaviour of coconut fibre-based green composites
(Foundation for Materials Science and Engineering “Serban Solacolu”, 2012)
This paper presents the influence of natural fibre content on the mechanical properties of coconut fibre based-green composites. The mixture ratio of cement:sand by weight was fixed at 1:1. Coconut fibre was used as ...
Composite cement reinforced coconut fiber: physical and mechanical properties and fracture behavior
(INSInet Publications, 2011)
This research paper reports the effect of natural fiber content on the physical and mechanical properties as well as fracture behavior of composite cement reinforced with coconut fiber. The mix design was based on 1:1 for ...
Effect of space holder and compaction pressure on the porosity of sintered copper
(Trans Tech Publications, 2013)
The effect of space-holder content on the porosity of sintered copper that was fabricated by powder metallurgy technique has been investigated. Carbamide was used as space-holder and the content selected was 10 wt. %, 20 ...
Comparative study on thermal, compressive, and wear properties of palm slag brake pad composite with other fillers
(Trans Tech Publications, 2011)
The attractive performance-to-cost ratio associated with the incorporation of waste material in composite formulations used to produce brake pads has stimulated the idea of exploring the possible incorporation of additional ...
Assessment of physical and mechanical properties of cement panel influenced by treated and untreated coconut fiber addition
(Elsevier BV, 2011)
This project was conducted to produce a cement panel with the addition of treated and untreated coconut fiber in cement panel. Coconut fiber was added to replace coarse aggregate (sand) in this cement panel. In this project, ...