    • Fabrication and characterization of porous F-75 for potential application in tissue engineering 

      Shamsul Baharin,  Jamaludin, Prof. Dr.; Tan, Wei Leng; Nur Hidayah, Ahmad Zaidi; Zuraidawani, Che Daud; Mazlee, Mohd Noor, Dr. (Trans Tech Publications, 2013)
      Porous F-75 (Co-Cr-Mo) was produced by powder metallurgy technique. F-75 powder was mixed with space holder and compacted using different pressures (300 MPa, 350 MPa, 400 MPa, 450 MPa). The green samples were sintered at ...
    • Response of functionality graded hydroxyapatite/F-75 in saline solution 0.9% NaCl 

      Noorazimah, Mohd Ab Llah; Shamsul Baharin,  Jamaludin, Prof. Dr.; Nur Hidayah, Ahmad Zaidi (Trans Tech Publications, 2013)
      Functionally graded hydroxyapatite (HAP) /F-75 was fabricated using powder metallurgy technique. Samples fabricated were tested inside 0.9% NaCl to check their bioactivity reaction. After immersed, samples were analyzed ...