The influence of CB, silica and CaCO₃ on tensile and morphological properties of vPE/rPE/EPDM blends
![No Thumbnail [100%x80]](data:image/svg+xml;base64,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)
Date
2014Metadata
Show full item recordAbstract
The virgin polyethylene (vPE) and recycled polyethylene (rPE) was melt blended with ethylene propylene diene terpolymer (EPDM) in different ratio by using a Haake Rheomix at 180°C and 50 rpm were prepared. The characterization such as tensile properties and morphology were examined. Results indicated that, the tensile strength and youngs modulus of vPE/rPE/EPDM with CB show the highest value compared to silica and CaCO₃ except for elongation at break. The scanning electron microscopy (SEM) studies proved that, better dispersion and less agglomeration of CB and silica filled particles as compared to the CaCO₃.