Behaviour of stress corrosion cracking of austenitic stainless steels in sodium chloride solutions
(Malaysian Technical Universities Network (MTUN), 2012-11-20)
Click Stress Corrosion Cracking (SCC) is an environmentally well-known as a failure caused by exposure to a corroding while under a sustained tensile stress. SCC is most often rapid, unpredictable. Failure can occur in a ...
Effect of roughness of hypo-and hyper-eutectic Al-Si piston alloy on wear characteristics under lubrication
(Malaysian Technical Universities Network (MTUN), 2012-11-20)
The tribological behavior of tow AlSi alloys under the influence of surface roughness average was investigated for the present study. The silicon content of these alloys ranged 10 and 16-wt% Si, and includes hypoeutectic ...
The effect of austenite temperature on the fatigue strength of mild steel
(Universiti Malaysia Perlis (UniMAP), 2012-02-27)
The effect of austenite temperature on the fatigue strength of
mild steel is investigated by using the Scanning Electron
Microscopic (SEM). Fatigue tests under the rotating bending
fatigue testing machine has been carried ...
Stress corrosion cracking behavior of austenitic stainless steels in natrium chloride solution
(Universiti Malaysia Perlis (UniMAP), 2010-10-16)
Stress corrosion cracking (SCC) of austenitic
stainless steels of types 304, 310 and 316 will be
investigated as a function of applied stress at room
temperature in natrium chloride solutions under a
constant applied ...