Effect of Solution Treatment Temperature on Recycled Aluminium Alloy 319
Date
2007-06-09Author
Murizam Darus
Shamsul Baharin Jamaludin, Assoc. Prof. Dr.
Metadata
Show full item recordAbstract
In the present work, the responses of artificial ageing process to different solutionising temperatures on recycled 319 series aluminium alloy are studied. The optimisation of solutionising temperature may lead to the formation of higher volumes of precipitates in the aluminium alloy during the artificial ageing process, which means the greater strength to the alloy. The aluminium alloy samples were sectioned from
recycled automotive cylinder head and solutionised at three different solutionising temperatures, stated as 495°C, 510°C and 525°C for 10 hours. All samples were then artificially aged at 180°C for a period of 20 hours. The precipitation behaviour was monitored by Vicker’s microhardness test and electrical resistivity
measurement. The result showed that all solutionising temperature produced double peaks on the artificial ageing hardness profiles but at different ageing time. The similar trend was also observed by the
resistivity measurement.
Collections
- Conference Papers [2600]
- Murizam Darus, Mr. [17]
Related items
Showing items related by title, author, creator and subject.
-
The effect of duration aging temperature on fatigue strength of aluminum alloy strength of aluminum alloy
Ahmad Syayuthi, Abdul Rahman; Haftirman; Teo, Ee Lynn (Universiti Malaysia Perlis (UniMAP)Pusat Pengajian Kejuruteraan Mekatronik, 2012-02-27)This paper present the effect of different duration aging temperature on fatigue strength of Al6063. Al 6063 alloy specimens have been solution heat treated at 520C for 2 hours. Subsequently, the artificial ageing heat ... -
Structural and phase formation of TiAl alloys synthesized by mechanical alloying and heat treatment
Al-Dabbagh, Jinan B.; Rozman, Mohd Tahar; Mahadzir, Ishak; Siti Aisyah, Harun (Universiti Malaysia Perlis, 2015)Mechanical alloying (MA) of Ti-50%Al (molar fraction) powder by using Planetary ball milling equipment, have been successfully refine the crystallite size and produced TiAl nano-alloys. The characteristics of the powder ... -
Preparation of submicron Al-Ti Alloy particles by mechanical alloying
Abdul Razak, Daud; Adolf Asih, Supriyanto (Universiti Malaysia Perlis, 2009-12-01)Introduction: Mechanical alloying (MA) is a solid-state powder processing technique involving repeated welding, fracturing and re-welding of powder particles in a high-energy ball mill [1-3]. MA has been used to synthesize ...