Oxidation behaviour of Sodium and Potassium choride coated Fe-C alloy at 400-700°C
(Oriental Science Publishing Company, 2003)
The studies have been conducted on the oxidation behaviour of Fe-C alloy at 400 to 700 °C in presence of alkali metal chloride salts such as sodium chloride and potassium chloride. The chloride compounds decompose at high ...
Oxidation behaviour of 8.6 Al-Cu alloy in South China Seawater
(Sadguru Publications, 2005)
The corrosion behavior of 8.6 Al-Cu alloy was investigated in 4 different conditions of South China Seawater. The weight loss curve of alloy increases with time during the initial exposure period, due to dissolution of ...
The CsCl- and CsN03-induced high temperature oxidation of Nimonic-90 alloy at 1123 K
(Elsevier Science B.V., 1996)
Nickel-base alloys find vital scope in space and nuclear applications due to their numerous favourable properties such as low density, high strength and corrosion resistance. The high temperature oxidation of Nimonic-90 ...
Oxidation behaviour of AISI-304 steel in the presence of Na2S04 and Fe2(S04)3 at 973 K
(Elsevier Science B.V., 1994)
The high temperature oxidation behaviour of AISI-304 austenitic steel was studied in the presence of Na2S04, Fe2(S04)3 or a mixture at 973 K in flowing air. The studies were carried out to examine the influence of eutectic ...
Effect of some sodium salts coatings on the high-temperature oxidation of Nimonic-80A alloy at 1173 K
(Elsevier Science B.V., 1997)
The effects of some sodium salts, namely Na2S04, NaCl, NaN03 and Na2C03 coatings, on the high-temperature oxidation behaviour of Nimonic-80A (N-80A) alloy at 1173 K in a slow current of air are presented. The oxidation ...
Hot corrosion of austenitic steel in Molten alkali sulphate deposits at 850°C
(Carl Hanser Verlag, 1996)
Oxidation behavior of Sodium-, Calcium- and Potassium- Sulphates coated Fe-20Cr alloy at 800°C
(Chinese Electronic Periodical Services, 1997-04)
The effect of Na2S04, CaS04,K2S04 and their mixture coatings on the high temperature oxidation behaviour of Fe-20Cr alloy at 800 C has been investigated. The data have been complemented by kinetic measurements, SEM ...
Effect of Sodium Nitrate and Sodium Peroxide deposits on high temperature oxidation of Nimonic-105 Alloy at 700 C *
(Chinese Electronic Periodical Services, 1995)
The effect of sodium nitrate (NaN03) and sodium peroxide (Na202) deposits on the high temperature oxidation of Nimonic-105 (N-105) alloy at 700rj has been studied for a period of 120 h in air. The alloy was more severely ...
Effect of Na2SO4 and Fe2(SO4)3 on the oxidation behaviour of AISI-303 Alloy at 900°
(Africa Journals Online, 1993)
The effects of NajS04 and Fe2(S04)3 coatings on the oxidation behaviour of AISI-303 alloy at 900° has been studied in flowing air. The coated samples were oxidised for a period up to 24 hr. The oxidation rate increased ...
Oxidation behavior of SAE-1053 alloy in presence of seawater
(INSInet Publication, 2009-01)
The oxidation behavior of steel SAE-1053 alloy were investigated in presence of seawater at atmospheric condition. The rate of corrosion was varied with the water movements and the aeration. The scale morphologies were ...