Review on fly ash-based geopolymer concrete without portland cement
(Universiti Malaysia Perlis (UniMAP), 2010-10-16)
This paper summarizes the factors that affect the properties of fly ash-based geopolymer concrete. Alkaline activator is an important material that controls the properties of geopolymer concrete. The workability of fresh ...
Effect of curing regimes on metakaolin geopolymer pastes produced from geopolymer powder
(Scientific.Net/Trans Tech Publications, 2012-12)
The properties of metakaolin geopolymer paste are affected by the alkali concentration, the initial raw materials, solidification process, and amount of mixing water as well as the curing conditions. This study aimed to ...
Strength and microstructural properties of mechanically-activated kaolin geopolymers
(Trans Tech Publications, 2012-12)
Kaolin geopolymers exhibit low strength properties due to its plate-like nature which contribute to smaller surface area for geopolymerization reactions. Layered kaolin structure only allows very little, if any, substitution ...
Mechanical performances of fly ash geopolymer bricks
(American Scientific Publishers, 2013-01)
Geopolymer is a new class of three-dimensionally networked amorphous to semi-crystalline alumino-silicate materials, and first developed by Professor Davidovits in 1978. Geopolymers can be synthesized by mixing alumino-silicate ...
Lightweight fly ash-based geopolymer concrete
(Trans Tech Publications, 2013)
The experiments of this study were preformed to study the synthesis process for lightweight aggregate geopolymer concrete (LWAGC) using normal sand as a fine aggregate and expanded clay as lightweight aggregate. The LWAGC ...
A study on the synthesis of fly ash-based lightweight aggregate geopolymer concrete
(American Scientific Publishers All rights reserved., 2013-01)
The experiments conducting for current investigation aimed to study the synthesis process for lightweight aggregate geopolymer concrete (LWAGC) and explore the significance and limitations of the activator content on the ...
Fire resistance evaluation of lightweight geopolymer concrete system exposed to elevated temperatures of 100-800 °C
(Trans Tech Publications, 2014)
This paper reports the fire resistance property of a lightweight aggregate geopolymer concrete (LWAGC) material synthesized by the alkali-activation of locally source fly ash (FA) after exposed to elevated temperatures ...
Investigating the possibility of utilization of kaolin and the potential of metakaolin to produce green cement for construction purposes-A review
(INSInet Publication, 2011-09)
Geopolymers are inorganic alkali aluminosilicate gels, formed from reaction of mineral clays or aluminosilicate-bearing industrial wastes, and treated with alkali silicate solution at 40-80°C. Geopolymers have been studied ...
Microstructure study on optimization of high strength fly ash based geopolymer
(Trans Tech Publications, 2012)
The compressive strength and microstructural characteristics of fly ash based geopolymer with alkaline activator solution were investigated. The sodium hydroxide and sodium silicate were mixed together to form an alkaline ...
Microstructure study on volcano ash geopolymer aggregate at different sintering temperature
(Trans Tech Publications, 2014)
Recent research shows that the by-product materials such as fly ash can be used as raw material in producing aggregates and lightweight aggregates. The usage of this material can improve the quality of the aggregates ...