Effect of NaOH concentration on microstructure of boiler ash based geopolymer
(Trans Tech Publications Ltd., 2015)
Boiler ash is one of the waste material from palm oil processing industry and it was widely available. The role of alkaline activator in geopolymer is important for its mechanical properties. NaOH and sodium silicate ...
Chemical and physical characterization of boiler ash from palm oil industry waste for geopolymer composite
(Syscom 18 SRL/ SC BIBLIOTECA CHIMIEI SA, 2013-12)
The characterizations of boiler ash waste from waste of palm oil industry were performed. The boiler ash was obtained from the boiler in the palm oil processing factory. The chemical and physical characterization has been ...
The relationship of NaOH molarity, Na2SiO3/NaOH ratio, fly ash/alkaline activator ratio, and curing temperature to the strength of fly ash-based geopolymer
(Trans Tech Publications, 2011)
Geopolymer, produced by the reaction of fly ash with an alkaline activator (mixture of Na2SiO3 and NaOH solutions), is an alternative to the use of ordinary Portland cement (OPC) in the construction industry. However, there ...
Effect of Solids-To-Liquids, Na2SiO3-To-NaOH and Curing Temperature on the Palm Oil Boiler Ash (Si + Ca) Geopolymerisation System
(MDPI AG, 2015)
This paper investigates the effect of the solids-to-liquids (S/L) and Na2SiO3/NaOH ratios on the production of palm oil boiler ash (POBA) based geopolymer. Sodium silicate and sodium hydroxide (NaOH) solution were used as ...
The effect of curing temperature on physical and chemical properties of geopolymers
(Elsevier BV, 2011)
Fly ash-based geopolymers required heat to increase the geopolymerization process in order to obtain higher compressive strength. As such, geopolymer samples were prepared using different curing temperatures (room temperature, ...
Strength, density and water absoprtion of Palm oil boiler ash (POBA) geopolymer brick/IBS brick
(Trans Tech Publications Ltd., 2016-01)
Geopolymer or alkali-activated binder is produced by synthesizing aluminosilicate source materials with an alkaline activator solution. This study has been conducted to produce palm oil boiler ash (POBA) geopolymer brick/IBS ...
Optimization of NaOH Molarity, LUSI Mud/Alkaline Activator, and Na2SiO3/NaOH Ratio to Produce Lightweight Aggregate-Based Geopolymer
(MDPI AG, 2015-05-21)
This paper presents the mechanical function and characterization of an artificial lightweight geopolymer aggregate (ALGA) using LUSI (Sidoarjo mud) and alkaline activator as source materials. LUSI stands for LU-Lumpur and ...