Effect of NaOH concentration on microstructure of boiler ash based geopolymer
(Trans Tech Publications Ltd., 2015)
Boiler ash is one of the waste material from palm oil processing industry and it was widely available. The role of alkaline activator in geopolymer is important for its mechanical properties. NaOH and sodium silicate ...
Chemical and physical characterization of boiler ash from palm oil industry waste for geopolymer composite
(Syscom 18 SRL/ SC BIBLIOTECA CHIMIEI SA, 2013-12)
The characterizations of boiler ash waste from waste of palm oil industry were performed. The boiler ash was obtained from the boiler in the palm oil processing factory. The chemical and physical characterization has been ...
Microstructure study on optimization of high strength fly ash based geopolymer
(Trans Tech Publications, 2012)
The compressive strength and microstructural characteristics of fly ash based geopolymer with alkaline activator solution were investigated. The sodium hydroxide and sodium silicate were mixed together to form an alkaline ...
Microstructure study on volcano ash geopolymer aggregate at different sintering temperature
(Trans Tech Publications, 2014)
Recent research shows that the by-product materials such as fly ash can be used as raw material in producing aggregates and lightweight aggregates. The usage of this material can improve the quality of the aggregates ...
Influence of dolomite on the mechanical properties of boiler ash geopolymer paste
(Trans Tech Publications, 2014)
The waste material from palm oil industry has been increasing since Malaysia was the world largest exported of palm oil mill. The waste such as palm fibers, nut shells, palm kernel and empty fruit bunches are the solid ...
The relationship of NaOH molarity, Na2SiO3/NaOH ratio, fly ash/alkaline activator ratio, and curing temperature to the strength of fly ash-based geopolymer
(Trans Tech Publications, 2011)
Geopolymer, produced by the reaction of fly ash with an alkaline activator (mixture of Na2SiO3 and NaOH solutions), is an alternative to the use of ordinary Portland cement (OPC) in the construction industry. However, there ...
Effect of Solids-To-Liquids, Na2SiO3-To-NaOH and Curing Temperature on the Palm Oil Boiler Ash (Si + Ca) Geopolymerisation System
(MDPI AG, 2015)
This paper investigates the effect of the solids-to-liquids (S/L) and Na2SiO3/NaOH ratios on the production of palm oil boiler ash (POBA) based geopolymer. Sodium silicate and sodium hydroxide (NaOH) solution were used as ...
Reviews on the properties of aggregates made with or without geopolymerisation method
(Scientific.Net/Trans Tech Publications, 2012-12)
Aggregates are popular for use in concrete and lightweight concrete applications. Recent research shows that the by-product materials such as fly ash can be used as raw material in producing aggregates and lightweight ...
Fly ash-based geopolymer lightweight concrete using foaming agent
(MDPI, Basel, Switzerland., 2012-06)
In this paper, we report the results of our investigation on the possibility of producing foam concrete by using a geopolymer system. Class C fly ash was mixed with an alkaline activator solution (a mixture of sodium ...
The effect of curing temperature on physical and chemical properties of geopolymers
(Elsevier BV, 2011)
Fly ash-based geopolymers required heat to increase the geopolymerization process in order to obtain higher compressive strength. As such, geopolymer samples were prepared using different curing temperatures (room temperature, ...