    • The effect of curing time on the properties of fly ash-based geopolymer bricks 

      Wan Mastura, W. I.; Kamarudin, Hussin, Brig. Jen. Datuk Prof. Dr.; Khairul Nizar, Ismail, Prof. Madya Dr.; Mohd Mustafa Al Bakri, Abdullah; Mohammed, Bnhussain (Scientific.Net/Trans Tech Publications, 2012-12)
      This paper reports the results of an experimental work conducted to investigate the effect of curing conditions on the properties of fly ash-based geopolymer bricks prepared by using fly ash as base material and combination ...
    • The influence of curing periods on the compressive strength of fly ash-based geopolymer at different aging times 

      Omar A., Abdulkareem; Mohd Mustafa Al-Bakri, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Khairul Nizar, Ismail, Prof. Madya Dr. (Trans Tech Publications, 2012)
      The results of the current experimental investigation indicate the significant effect of the heating periods on the compressive strength of fly ash-based geopolymers prepared at different alkaline liquid content at both ...
    • Processing and characterization of calcined kaolin cement powder 

      Liew, Yun Ming; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al Bakri, Abdullah; Luqman, Musa, Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Che Mohd Ruzaidi, Ghazali; Cheng, Yong Heah (Elsevier Ltd, 2012-05)
      Abstract This paper aimed at investigating the possibility of calcined kaolin to produce cement powder that could be an alternative to Portland cement by applying geopolymerization process. Cement paste was firstly made ...
    • Properties of metakaolin geopolymeric binder 

      Liew, Yun Ming; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al Bakri, Abdullah; Mohamed, Bnhussain, Prof. Dr.; Luqman, Musa, Dr.; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Che Mohd Ruzaidi, Ghazali, Prof. Madya; Heah, Cheng Yong (American Scientific Publishers, 2013-01)
      This paper investigates the physical and mechanical properties as well as the morphology study of the MK geopolymeric binder. Mixture of waterglass liquid and NaOH solution were used as the activator solution for the ...
    • Strength and microstructural properties of mechanically-activated kaolin geopolymers 

      Cheng, Yong Heah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Mohd Mustafa Al Bakri, Abdullah; Mohammed, Bnhussain; Luqman, Musa; Khairul Nizar, Ismail; Che Mohd Ruzaidi, Ghazali, Prof. Madya; Liew, Yun Ming (Trans Tech Publications, 2012-12)
      Kaolin geopolymers exhibit low strength properties due to its plate-like nature which contribute to smaller surface area for geopolymerization reactions. Layered kaolin structure only allows very little, if any, substitution ...
    • Study on solids-to-liquid and alkaline activator ratios on kaolin-based geopolymers 

      Cheng, Yong Heah; Kamarudin, Hussin, Brig. Gen. Dato' Prof. Dr.; Mohd Mustafa Al-Bakri, Abdullah; Mohammed, Hussain; Luqman, Musa; Khairul Nizar, Ismail, Assoc. Prof. Dr.; Che Mohd Ruzaidi, Ghazali; Liew, Yun Ming (Elsevier Ltd., 2012-10)
      Kaolin and alkali activator were mixed with the solids-to-liquid ratios in range of 0.60-1.20 (Al 2O 3/Na 2O molar ratio of 0.63-1.27). Sodium silicate and sodium hydroxide ranged between 0.16 and 0.36 (SiO 2/Na 2O molar ...