The Effect of Lubrication Agent in Fabrication of Recycled Steel Powder using Ball Milling from Machining Steel Chips
(Universiti Malaysia Perlis (UniMAP), 2007-06-09)
A feasibility study for producing recycled steel powder from steel scrap by ball milling was carried out. Steel scrap from machining was used as a raw material and was milled using ball milling for 40 hours. It
was found ...
The Effect of Milling Time on Microstrucutre and Hardness of the Aluminium Silicon Carbide (Al-10 wt % SiCp) Composite
(Universiti Malaysia Perlis (UniMAP), 2007-06-09)
The aim of this study is to develop Al – 10 wt % SiCp composite by powder metallurgy technique. Aluminium and SiC powder were mixed by ball milling and it was then sintered at 550° C for 5 hours. The parameter to control ...
The Microsructure and Properties of Aluminium Composite Reinforced with 65 μm Alumina Particles via Powder Metallurgy
(Universiti Malaysia Perlis (UniMAP), 2007-06-09)
This article will report the effect of weight percentage on the microstructure and properties of alumina particle reinforced aluminum metal matrix composite. This involved fabrication of aluminum composite
via powder ...
Effect of Particle Coating on Matrix-Reinforcement Bonding
(Universiti Malaysia Perlis (UniMAP), 2007-06-09)
A crucial step in the liquid state processing of particulates reinforced metal matrix composites is the incorporation of the ceramic particles into molten matrix alloy. The development of SiO2 coating on fly
ash particles ...
Study of Spot Welding of Austenitic Stainless Steel Type 304
(Universiti Malaysia Perlis (UniMAP), 2007-06-09)
In this study, austenitic stainless steel type 304 were welded by resistance spot welding. The relationship of nugget diameter and welding current was investigated. Hardness distribution along welding zone was
also ...
Effect of Colloidal SIO2 Content on the Morphology of Coated Ceramic Particles
(Universiti Malaysia Perlis (UniMAP), 2007-06-09)
Coated structure on fly ash particles was produced by liquid stirring of colloidal SiO2. Morphological study by means of scanning electron microscope has consent to controlling the present of outer layer by
the addition ...
The effect of intermediate stop and ball size in fabrication of recycled steel powder using ball milling from machining steel chips
(Universiti Teknologi Malaysia (UTM), 2007-11-30)
A feasibility study for producing recycled
steel powder from steel scrap by ball milling was carried out. Steel scrap from machining was used as a raw material and was milled using planetary ball milling. Three samples ...
Effect of Milling Periods on the Iron Mill Scale Particle Size and Properties
(Universiti Malaysia Perlis (UniMAP), 2007-06-09)
The relations between the milling periods with the iron mill scale particle size have been studied. Iron mill scale has been chosen for this research due to the nature of itself, as a by-product. From this
research, the ...