Controllable oxidization of boron doped nanodiamond covered with different solution via UV/ozone treatment
(Elsevier B.V., 2012-04)
UV/ozone irradiation was designed for controllable oxidation of nanodiamond films with distinctive chemical species. XPS investigation revealed that various kinds of oxygen-related chemical components would be functionalized ...
Oxidation behaviour of mild steel in molten alkali metal salts deposits
(ASEAN Committee on Science & Technology, 2003-06)
The oxidation behaviour of commercial mild steel has been investigated in presence of alkali metal salts viz. NaCl, Na2CC>3, KC1, K2CO3 in the temperature at 750°C for the period of 36 h in atmospheric condition. The low ...
Oxidation behavior of AISI 304 steel in presence of Na2 SO4 and K2 SO4 at 900°C
(Carl Hanser Verlag, 1993)
Steels with high Cr- and Ni-contents utilized at elevated temperatures are oxidation resistant due to the formation of slowly growing, protective chromium oxide layers [1,2]. Na2SO4 or K2SO4 alone or in synergistic combination ...
Oxidation behavior of Sodium-, Calcium- and Potassium- Sulphates coated Fe-20Cr alloy at 800°C
(Chinese Electronic Periodical Services, 1997-04)
The effect of Na2S04, CaS04,K2S04 and their mixture coatings on the high temperature oxidation behaviour of Fe-20Cr alloy at 800 C has been investigated. The data have been complemented by kinetic measurements, SEM ...
Effect of Sodium Nitrate and Sodium Peroxide deposits on high temperature oxidation of Nimonic-105 Alloy at 700 C *
(Chinese Electronic Periodical Services, 1995)
The effect of sodium nitrate (NaN03) and sodium peroxide (Na202) deposits on the high temperature oxidation of Nimonic-105 (N-105) alloy at 700rj has been studied for a period of 120 h in air. The alloy was more severely ...
Effect of Na2SO4 and Fe2(SO4)3 on the oxidation behaviour of AISI-303 Alloy at 900°
(Africa Journals Online, 1993)
The effects of NajS04 and Fe2(S04)3 coatings on the oxidation behaviour of AISI-303 alloy at 900° has been studied in flowing air. The coated samples were oxidised for a period up to 24 hr. The oxidation rate increased ...
Oxidation behavior of SAE-1053 alloy in presence of seawater
(INSInet Publication, 2009-01)
The oxidation behavior of steel SAE-1053 alloy were investigated in presence of seawater at atmospheric condition. The rate of corrosion was varied with the water movements and the aeration. The scale morphologies were ...