Study on the geopolymer concrete properties reinforced with hooked steel fiber

Abstract

In this research, Class F fly ash and a mixture of alkaline activators and different amount of hooked steel fiber were used for preparing geopolymer concrete. In order to analyses the effect of hooked steel fiber on the geopolymer concrete, the analysis such as chemical composition of fly ash, workability of fresh geopolymer, water absorption, density, compressive strength of hardened geopolymer concrete have been carried out. Mixtures were prepared with fly ash to alkaline liquid ratio of 2.0 with hooked steel fibers were added to the mix with different amounts which are 1%, 3%, 5% and 7% by the weight of the concrete. Experimental results showed that the compressive strength of geopolymer concrete increases as the hooked steel fibers increases. The optimum compressive strength obtained was up to 87.83 MPa on the 14th day. The density of geopolymer concrete are in the range between 2466 kg/m³ to 2501 kg/m³. In addition, the workability value of geopolymer without hooked steel fibers is 100 mm while the workability value of geopolymer with hooked steel fibers are between 60 mm to 30 mm.