Title: | Preparation, characterization, and electrical conductivity investigation of multi-walled carbon nanotube-filled composite nanofibres |
Authors: | A. H. Nurfaizey N. A. Munajat S. R. Esa M. A. Salim A. M. Saad M. A. M. Rosli N. Tucker nurfaizey@utem.edu.my |
Issue Date: | Aug-2021 |
Publisher: | Universiti Malaysia Perlis (UniMAP) |
Citation: | International Journal of Nanoelectronics and Materials, vol.14(Special Issue), 2021, pages 191-200 |
Abstract: | There is a growing interest in carbon nanofibre materials especially for applications that require high surface area, excellent chemical inertness, and good electrical conductivity. However, in certain applications a much higher electric conductivity is required before one can take the full advantage of the nanofibre network. Therefore, incorporating superconductive materials such carbon nanotubes is thought to be a feasible approach to enhance the electrical properties of the carbon nanofibres. The objectives of this study were to prepare and characterize multi-walled carbon nanotube-filled composite nanofibres. Carbon nanofibres were produced via electrospinning technique using precursor solutions of polyacrylonitrile in dimethylformamide loaded with different amount of multi-walled carbon nanotubes (MWCNT). The electrospun fibre samples were then pyrolyzed in a nitrogen-filled laboratory tube furnace. Characterization process was performed using scanning electron microscope (SEM), transmission electron microscope (TEM), and fourpoint probe method. It was found that the incorporation of MWCNT into the carbon nanofibre structures could significantly increase the electric properties of the nanofibres. The composite nanofibres with 0.1 wt.% of MWCNT loading has the highest electrical conductivity of 155.90 S/cm compared to just 10.71 S/cm of the pure carbon nanofibres. However, the electrical conductivity of the composite fibres reduced drastically when higher weight percentages of MWCNT were used. This was caused by agglomeration of MWCNT causing premature percolation, and broken fibre network as evidenced by SEM and TEM examinations. The results obtained from this study may facilitate improvements in the development of superconductive high surface area materials for electronic applications. |
Description: | Link to publisher's homepage at http://ijneam.unimap.edu.my |
URI: | http://dspace.unimap.edu.my:80/xmlui/handle/123456789/73684 |
ISSN: | 1985-5761 (Printed) 1997-4434 (Online) |
Appears in Collections: | International Journal of Nanoelectronics and Materials (IJNeaM) |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Preparation, Characterization, and Electrical Conductivity.pdf | Main article | 2.03 MB | Adobe PDF | View/Open |
Items in UniMAP Library Digital Repository are protected by copyright, with all rights reserved, unless otherwise indicated.