Title: | The anodizing of sintered Mg/Ca alloys |
Authors: | Norhadira Fatin, Wardi Dr. Zuraidawani Che Daud |
Keywords: | Anodizing Materials engineering Alloys Mg/Ca alloys Biomaterials Powder metallurgy |
Issue Date: | Jun-2016 |
Publisher: | Universiti Malaysia Perlis (UniMAP) |
Abstract: | This project is focusing on the effect of anodizing on the sintered Mg/Ca alloys. The Mg/Ca alloy was fabricated using powder metallurgy method. The Mg powder was mixed with 1 wt.% Ca powder using rotating mill with ball powder ration of 10:1 for 1 hour with speed of 100 rpm. The mixed powder was compacted using pressure of 200 MPa and then sintered using tube furnace in argon atmosphere at 550oC for 60 minutes. The anodizing process was carried out using two different parameters which are voltage (5V, 15V, 25V) and KOH concentration (0.1M, 0.5M, 1.0M) for 1 hour. Both anodized and non-anodized samples were analyzed using several analysis such as mass change per surface area, density test, mass percentage of compound formation, surface analysis, hardness test, and X-Ray Diffraction (XRD) analysis. From this study, it is found that different anodizing parameter affected the hardness of the samples. |
Description: | Access is limited to UniMAP community. |
URI: | http://dspace.unimap.edu.my:80/xmlui/handle/123456789/48076 |
Appears in Collections: | School of Materials Engineering (FYP) |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Abstract,Acknowledgement.pdf | 154.7 kB | Adobe PDF | View/Open | |
Introduction.pdf | 132.04 kB | Adobe PDF | View/Open | |
Literature Review.pdf | 424.63 kB | Adobe PDF | View/Open | |
Methodology.pdf | 999.7 kB | Adobe PDF | View/Open | |
Results and Discussion.pdf | 3.7 MB | Adobe PDF | View/Open | |
Conclusion and Recommendation.pdf | 123.28 kB | Adobe PDF | View/Open | |
Refference and Appendics.pdf | 245.94 kB | Adobe PDF | View/Open |
Items in UniMAP Library Digital Repository are protected by copyright, with all rights reserved, unless otherwise indicated.