Optical characterization of SixGe1-x films grown on nanostructured Si substrates
Date
2014-10-15Author
Ayu Wazira, Azhari
Adnan K Shafeeque, Ali
Kamaruzzaman, Sopian
Saleem Hussain, Zaidi
Uda, Hashim
Metadata
Show full item recordAbstract
High quality Ge and SixGe1-x films grown on Si substrates are attractive for a wide range of applications in optics, optoelectronics, and high efficiency solar cells. In this study, heteroepitaxial growth of Ge on nanostructured Si surfaces has been investigated. Thermally evaporated amorphous Ge films are vacuum-deposited and crystallized by thermal annealing at 1000 °C. Scanning electron microscope (SEM), spectroscopy (RS), infrared (IR) transmission, and Raman methods are used to characterize amorphous and crystalline Ge films. SEM analysis reveals presence of dominant features including cracks, microscopic roughness, and islands. RS exhibits strong multiple peaks attributed to crystalline structures related to Si-Ge at ∼ 444 cm-1 and Ge at 300 cm-1; narrow and stronger peaks are observed in thermally annealed films. A comparison of IR transmission measurements in 900-1700-nm spectral range shows that amorphous film absorption is significantly higher than that of crystalline films consistent with respective bandgaps. A more detailed analysis including EDX and XRD measurements will be presented at the conference.