An AZ91D ingot in the as-cast condition was homogenized by heat treatment process. Then, the microstructures produced and corrosion behaviour after heat treatment was studied in detail. As-cast AZ91D was recrystallize by ...

Oxide coatings on AZ91D magnesium alloy were prepared using anodizing technique with 10mA/cm2 current density for 5 minutes in electrolyte containing Mg (NO₃)₂ with NaVO₃ as an additive. The corrosion behaviors of different ...

Pure Mg and AZ91D alloy was anodized with and without the gadolinium nitrate Gd(NO3)3 in different concentrations (0.001g/l, 0.025g/l, 0.05g/l, 0.075g/l and 0.09g/l) at a constant current density and treatment time of ...

An oxide film was prepared on AZ91D magnesium alloy by anodizing in solution containing sodium metavanadate (NaVO3). The corrosion resistance of the substrate was investigated at a fixed current density 10 mA/cm2 for 5 ...