Now showing items 1-4 of 4

    • Alteration of solution treatment condition to the precipitation behaviour A319 alloy 

      Murizam, Darus; Shamsul, Baharin Jamaludin, Prof. Dr.; Mohd Arif Anuar, Mohd Salleh; Faizul, Che Pa; Ruhiyuddin, Mohd Zaki (Trans Tech Publications, 2013)
      The development of precipitate during ageing treatment of A319 alloy contributed significantly to the alloy strengthening mechanism. Two solution treatment temperatures which were set at 510°C and 525°C were subjected onto ...
    • Effect of pyrolysis temperature on the synthesis of carbon fiber from natural organic waste 

      Shahrizam, Saad; Faizul, Che Pa; Mohd Mustafa Al-Bakri, Abdullah; Ruhiyuddin, Mohd Zaki; Murizam, Darus (Trans Tech Publications, 2014)
      Carbon fibers are produced from natural sources of water hyacinth plants that have been dried, ground and sieved to three different particle sizes of 600 μm, 300 μm and less than 300 μm. Through the analysis of data obtained ...
    • Study on milling periods on the iron mill scale particle size and properties 

      Ruhiyuddin, Mohd Zaki; Faizul, Che Pa; Murizam, Darus; A. R. M., Nazri (Trans Tech Publications, 2013)
      The relations between the milling periods with the iron mill scale particle size have been studied. Iron mill scale has been chosen for this research due to the nature of itself, as a by-product. From this research, the ...
    • Synthesis and characterization of iron produced from iron mill scale 

      Ruhiyuddin, Mohd Zaki; Murizam, Darus; Khairel Rafezi, Ahmad, Dr. (Trans Tech Publications, 2014-01)
      In this project, iron mill scale has been used to produce iron powder that can be used within the Powder Metallurgy process. To achieve this objective, the iron mill scale needs to be refined. This involve the work of ...