Effect of melting temperatures on the crystallization and densification of 2.8MgO•1.5Al2O3•5SiO2 glass-ceramic synthesized from mainly talc and kaolin
(Elsevier B. V., 2010-02-03)Single phase α-cordierite with low sintering temperature was produced from 2.8MgO·1.5Al2O3·5SiO2 chemical formulation using mainly talc and kaolin. The effect of melting temperature to the densification, crystallization ... -
Thermal expansion coefficient and dielectric properties of non-stoichiometric cordierite compositions with excess MgO mole ratio synthesized from mainly kaolin and talc by the glass crystallization method
(Elsevier B. V., 2010-04-02)α-Cordierite phase in non-stoichiometric cordierite formulations was synthesized using mainly kaolin and talc, without sintering aids, via the glass crystallization route. MgO mole ratios in the formulations were varied ...