Behaviour of stress corrosion cracking of austenitic stainless steels in sodium chloride solutions
(Malaysian Technical Universities Network (MTUN), 2012-11-20)
Click Stress Corrosion Cracking (SCC) is an environmentally well-known as a failure caused by exposure to a corroding while under a sustained tensile stress. SCC is most often rapid, unpredictable. Failure can occur in a ...
Behaviour of stress corrosion cracking of austenitic stainless steels in sodium chloride solutions
(Elsevier B.V., 2013)
Click Stress Corrosion Cracking (SCC) is an environmentally well-known as a failure caused by exposure to a corroding while under a sustained tensile stress. SCC is most often rapid, unpredictable. Failure can occur in a ...
Effect of roughness of hypo-and hyper-eutectic Al-Si piston alloy on wear characteristics under lubrication
(Malaysian Technical Universities Network (MTUN), 2012-11-20)
The tribological behavior of tow AlSi alloys under the influence of surface roughness average was investigated for the present study. The silicon content of these alloys ranged 10 and 16-wt% Si, and includes hypoeutectic ...
Evaluate the effects of various surface roughness on the tribological characteristics under dry and lubricated conditions for Al-Si alloy
(Scientific Research Publishing Inc. All rights reserved., 2012-07)
The effect of surface roughness average of hypereutectic aluminum silicon alloys (with 16 wt% Si) on the friction and wear was investigated. Various surface roughness average (Ra) of different degrees was verified as well ...
Effect of roughness of hypo-and hyper-eutectic Al-Si piston alloy on wear characteristics under lubrication
(Elsevier B.V., 2013)
The tribological behavior of tow Al-Si alloys under the influence of surface roughness average was investigated for the present study. The silicon content of these alloys ranged 10 and 16-wt% Si, and includes hypoeutectic ...
Tribological properties of WS2 nanoparticles lubricants on aluminum-silicon alloy and carbon steels
(Walailak University, 2013-06)
The rheological properties of nanometric tungsten disulphide (WS2) nanoparticles oil lubricants and its tribological performance with two hypereutectic Al-Si alloy and carbon steel are examined. These two oils are used to ...
Stress corrosion cracking behavior of austenitic stainless steels in natrium chloride solution
(Universiti Malaysia Perlis (UniMAP), 2010-10-16)
Stress corrosion cracking (SCC) of austenitic
stainless steels of types 304, 310 and 316 will be
investigated as a function of applied stress at room
temperature in natrium chloride solutions under a
constant applied ...
The size effect on fatigue strength of structural steel materials in high-humidity environment
(Universiti Malaysia Perlis, 2009-10-11)
Fatigue tests under rotating bending fatigue testing machine has been carried out to estimate the size effect on fatigue
strength of structural steel materials in high-humidity environment. The size and geometry of the ...
Micro fatigue testing machine
(Malaysian Invention and Design Society (MINDS), 2012-05-17)