    • Compaction optimization of Sn-Cu-Si3N4via powder metallurgy route for composite solder fabrication 

      Muhamad Hafiz, Zan @ Hazizi; Mohd Arif Anuar, Mohd Salleh; Zainal Arifin, Ahmad, Prof.; Mohd Mustafa Al-Bakri, Abdullah; Alida, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr. (Trans Tech Publications, 2013)
      The aim of this study was to optimize the compaction process of a composite solder fabricated via powder metallurgy route, before details study were conducted in the next stage. Powder of Sn, Cu and Si3N4 were carefully ...

    • A comparative study of solder properties of Sn-0.7Cu lead-free solder fabricated via the powder metallurgy and casting methods 

      Mohd Arif Anuar, Mohd Salleh; Mohd Mustafa Al Bakri, Abdullah; Sandu, Andrei Victor; Norainiza, Saud; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; McDonald, Stuart D.; Nogita, Kazuhiro (Syscom 18 SRL, 2013-07)
      The properties of Sn-0.7Cu solder bulk prepared via the powder metallurgy (PM) method were investigated and compared with solder bulk fabricated through casting. Distinct microstructures were observed in both PM and casting ...

    • Effect of space holder and compaction pressure on the porosity of sintered copper 

      Shamsul Baharin, Jamaludin, Prof. Dr.; Chong, Xin Yi; Alida, Abdullah; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr. (Trans Tech Publications, 2013)
      The effect of space-holder content on the porosity of sintered copper that was fabricated by powder metallurgy technique has been investigated. Carbamide was used as space-holder and the content selected was 10 wt. %, 20 ...

    • Microstructure and interface analysis of glass particulate reinforced aluminum matrix composite 

      Shamsul Baharin,  Jamaludin, Prof. Dr.; Hadipramana, Josef; Mohd Fitri, Mohamad Wahid; Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.; Azmi, Rahmat, Prof. (Trans Tech Publications (TTP), 2013)
      A characterization of microstructure and interface was made on the composites Al- 4% Cu reinforced with 15 wt. % glass particulate. The composite was fabricated by powder metallurgy followed by solution treatment and ...