Browsing School of Materials Engineering (FYP) by Subject "Sinter (Metallurgy)"
Now showing items 1-8 of 8
-
The effect of Barium Oxide to the properties of natural Hidroxyapatite
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)This project reports the mechanical properties and the microstructure of composite materials made of hydroxyapatite, obtained from natural cow bone, and BaO (1,2 and 5 wt.%), which were sintered at different temperatures ... -
The effect of cooling condition on the microstructure and properties of Al-4.4Cu-0.8Si-0.5Mg powder compacts
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)The aim of this research is to study the effect of cooling condition on microstructure and properties of Al alloy. Powder compacts from a premixed commercial aluminium powder Al-4.4Cu-0.8Si-0.5Mg (wt %) grade have been ... -
The effect of sintering temperature on mechanical properties of natural and synthetic Hydroxyapatite with Alumina (1%) as an additive
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-05)A multi sintering temperature of hydroxyapatite (HA) will give an affect not only for the shape, composition and arrangement of the microstructure, but also to a high impact on mechanical properties of those samples. Natural ... -
Microstructure of development Al-Mg-Si-Cu powder metallurgy under different addition of Sn
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)This project involve 3 sample types that had labeled as Premix A (1%Sn addition), Premix B (1.5%Sn addition) and Premix C (2.0%Sn), each types have five samples. After compaction process measured the weight, thickness, ... -
Sintering atmosphere effect on Al-0.2Mg alloy
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)The effect of sintering atmosphere on mechanical properties and microstructure of Al-0.2Mg alloy were investigated. In this study, one type of parameter were used that was; different sintering atmosphere. Al and Mg were ... -
Sintering behavior and microstructural characterization of Aluminium copper powder compacts (Al- 4.4 Cu-0.8 Si-0.5 Mg Wt% ) alloy prepared by powder metallurgy
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-05)Powder Metallurgy (P/M) is a near net shape metal forming techniques used to manufacture part to close tolerance. In this research, aluminium copper alloy (Al-4.4%Cu- 0.8% Si-0.5%Mg) is prepared by using P/M method. In ... -
Study on different sintering temperature on the composite ferum and cobalt reinforced with silicon carbide
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)Particulate-reinforced metal matrix composites (MMCs) have become more attractive to researches because of the problem of anisotropy and high cost of fibre reinforced MMCs. This study involves the fabrication of MMCs with ... -
Synthesis and characterization of Fe-Al alloy with different sintering temperature
(Universiti Malaysia PerlisSchool of Materials Engineering, 2008-04)The iron aluminides Fe3Al and FeAl3 have been among the most widely studied intermetallics because of their low cost, low density, good wear resistance, ease of fabrication and resistance to oxidation and corrosion. A ...