| Title: | Microstructural study and differential scanning alorimetry analysis at elevated temperatures of uperheated as-cast A357 alloy |
| Authors: | Mazlee, Mohd Noor
Shamsul, Baharin Jamaludin, Prof. Dr.
Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.
Shaiful Rizam, Shamsudin |
| E-mail: | mazlee@unimap.edu.my |
| Keywords: | Endothermic peaks
Solidification structures
Superheating
A357
Alloy |
| Issue Date: | 2009 |
| Publisher: | University of Malaya |
| Citation: | International Journal of Mechanical and Materials Engineering, vol.4(2), 2009, pages 181-185 |
| Abstract: | The microstructure of superheated as-cast A357 alloy has been analysed to study the solidification structures of α-Al dendrites, eutectic Si particles and intermetallic compounds at different sections of the specimen. The primary dendritic arms are broken to globular and spherical shaped of α-Al dendrites due to the thermal effect of superheating thermal treatment. Differential scanning calorimetry showed faster formation of endothermic peaks of superheated as-cast A357 alloy relatively also believed to be attributed by superheating thermal treatment. The solidification sequence of superheated A357 alloy was same as Sr modified Al7Si-Mg alloy [4] except for the reaction involving Al5FeSi intermetallic compound which started with Liq. → Al dendrites followed by Liq. → Al + Si and lastly Liq. → Al + Si + Mg2Si + Al8FeMg3Si6. |
| Description: | Link to publisher's homepage at http://myais.fsktm.um.edu.my/ |
| URI: | http://myais.fsktm.um.edu.my/10304/1/MICROSTRUCTURAL_STUDY_AND_DIFFERENTIAL_SCANNING_ALORIMETRY_ANALYSIS_AT_ELEVATED_TEMPERATURES_OF_UPER.pdf
http://hdl.handle.net/123456789/8901 |
| ISSN: | 1823-0334 |
| Appears in Collections: | School of Materials Engineering (Articles)
Kamarudin Hussin, Brig. Jen. Dato' Prof. Dr.
|
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.
|