Title: Failure analysis and characterization of Ferrous-Base alloy exposed in seawater environment
Authors: Mohammed Misbahul Amin
Neelofar, Amin
Kamarudin, Hussin
Che Mohd Ruzaidi, Ghazali
Keywords: Ferrous-base alloy;Failure analysis;Characterization;Scanning electron microscopes;EDS;Steel, Stainless -- Corrosion;Seawater;Corrosion
Issue Date: 3-Dec-2008
Publisher: Universiti Kebangsaan Malaysia (UKM)
Citation: p.39-45
Series/Report no.: Malaysian Metallurgical Conference (MMC 2008
Abstract: Ferrous-base alloy are well-suited and widely used for a broad range of engineering applications such as structural steelwork, pipelines, vessels in refineries, thermal power plant establishment, etc. not for their corrosion resistance but for their reasonably good mechanical properties of strength, toughness, ductility and hardness; ease of fabrication and low cost. The study focused on determining the corrosion susceptibility of the ferrous-base alloy in presence of seawater environment in a stagnant condition under service condition. Corroded scraps ferrous-base alloy discarded after use in different seawater environments were collected for failure analysis to determine the causes of deterioration and degradation of alloy. The alloy samples as well as the deposits were investigated and characterized by using Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS) and Rockwell Hardness Test. The purpose is to trace the causes of failure mode; to check the nature and purity of the metal and corrosion deposits; to determine whether any unusual impurities has been present in the medium and to verify if the equipment confirms to the stated specification of fabrication and design. Immersed in seawater, the alloy of incomplete recrytallisation showed thick, loose and porous films, of which the outer layers contained a great amount of seawater species, and of which the underlying substrate was found with severe inter-granular, pitting & crevice corrosion
Description: Organized by Universiti Kebangsaan Malaysia (UKM), 3rd - 4th December 2008 at Danau Golf Club, Bangi, Selangor.
URI: http://hdl.handle.net/123456789/4259
Appears in Collections:Conference Papers
Kamarudin Hussin, Brig. Jen. Dato' Prof. Dr.

Files in This Item:

File Description SizeFormat
Failure analysis and characterization of Ferrous-BaseAccess is limited to UniMAP community.1.18 MBAdobe PDFView/Open
View Statistics

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

 

Valid XHTML 1.0! Perpustakaan Tuanku syed Faizuddin Putra, Kampus Pauh Putra, Universiti Malaysia Perlis, 02600, Arau Perlis
TEL: +604-9885420 | FAX: +604-9885405 | EMAIL: rujukan@unimap.edu.my Feedback