|Title: ||Wettability, electrical and mechanical properties of 99.3Sn-0.7Cu/Si 3N4 novel lead-free nanocomposite solder|
|Authors: ||Kamarudin, Hussin, Brig. Jen. Dato' Prof. Dr.|
Khairel Rafezi, Ahmad, Dr.
Mohd Arif Anuar, Mohd Salleh
Muhammad Hafiz, Hazizi
Zainal Arifin, Ahmad, Prof. Dr.
|Keywords: ||Composite;Electrical properties;Lead-free solder;Mechanical properties;Wettability|
|Issue Date: ||4-Jul-2011|
|Publisher: ||Trans Tech Publications|
|Citation: ||Advanced Materials Research , vol 277, 2011, pages 106-111|
|Abstract: ||A nanocomposite solder alloy with 99.3Sn-0.7Cu base alloy was successfully fabricated using the powder metallurgy route which consists of blending, compaction and sintering. Varying amount of nano size silicon nitride particulates were introduced as reinforcements to obtain a novel lead-free nanocomposite solder alloy. Following fabrication, the sintered nanocomposite solder were cut into thin solder disc and were analyzed in terms of their wettability, electrical and mechanical properties. Wettability, electrical and mechanical properties of the nanocomposite solder were compared to 99.3Sn-0.7Cu and 96.3Sn-3.0Ag-0.5Cu lead-free solder which were fabricated with the same method using powder metallurgy route. Wettability property of the nanocomposite solder was found to be in the accepted range with wettability angle below 45° similar to 99.3Sn-0.7Cu and 96.3Sn-3.0Ag-0.5Cu lead-free solder. Besides wettability, the results of electrical and mechanical properties analysis showed that additions of nano size Si3N4 had enhanced the strength and electrical conductivity of nanocomposite solder comparing to 99.3Sn- 0.7Cu and 96.3Sn-3.0Ag-0.5Cu lead-free solder.|
|Description: ||Link to publisher's homepage at www.ttp.net/|
|Appears in Collections:||Khairel Rafezi Ahmad, Dr.|
School of Materials Engineering (Articles)
Kamarudin Hussin, Brig. Jen. Dato' Prof. Dr.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.