Title: Synthesis and characterization of xMgO-1.5Al2O3-5SiO2 (x = 2.6-3.0) system using mainly talc and kaolin through the glass route
Authors: Banjuraizah, Johar
Hasmaliza, Mohamad
Zainal Arifin, Ahmad
???metadata.dc.contributor.url???: zainal@eng.usm.my
Keywords: Glasses;Crystallization;Powder diffraction;Dielectric properties;Thermal properties
Issue Date: 3-Oct-2011
Publisher: Elsevier B.V.
Citation: Materials Chemistry and Physics, vol. 129 (3), 2011, pages 910-918
Abstract: Three non-stoichiometric cordierite with compositions of xMgO-1.5Al2O3-5SiO2 (x = 2.6-3.0 mol) were synthesized using mainly talc and kaolin through the glass route. The densification and crystallization behaviors of these glass powders were investigated using DTA, dilatometer, and XRD. Samples were then heat treated at 900 °C for 2 h and further analyzed using XRD, CTE, FESEM, density and porosity tests, and also dielectric test to further investigate their properties. The 2.8MgO·1.5Al2O3·5SiO2 glass composition fully densified and crystallized into high purity α-cordierite at the heat treatment temperature. It exhibited lower CTE and dielectric constant compared to other composition, making it suitable for high frequency applications. Other formulations which contain multi crystalline phases require much higher temperatures for densification. The CTE value depends on the type of crystalline phase which exist in the sample, while the dielectric constant decreased with increasing MgO amounts in the sample compositions.
Description: Link to publisher's homepage at http://www.elsevier.com
URI: http://www.sciencedirect.com/science/article/pii/S0254058411004214
ISSN: 0254-0584
Appears in Collections:Banjuraizah Johar, Dr.
School of Materials Engineering (Articles)

Files in This Item:

File Description SizeFormat
Synthesis and characterization of xMgO-1.5Al2O 3-5SiO2 (x = 2.6-3.0) system using mainly talc and kaolin through the glass route.pdf41.98 kBAdobe PDFView/Open
View Statistics

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.


Valid XHTML 1.0! Perpustakaan Tuanku syed Faizuddin Putra, Kampus Pauh Putra, Universiti Malaysia Perlis, 02600, Arau Perlis
TEL: +604-9885420 | FAX: +604-9885405 | EMAIL: rujukan@unimap.edu.my Feedback